EVS-EN ISO 9227:2012

Corrosion tests in artificial atmospheres - Salt spray tests (ISO 9227:2012)

Üldinfo
Kehtetu alates 18.04.2017
Alusdokumendid
ISO 9227:2012; EN ISO 9227:2012
Tegevusala (ICS grupid)
77.060 Metallide korrosioon
Direktiivid või määrused
puuduvad
Standardi ajalugu
Staatus
Kuupäev
Tüüp
Nimetus
18.04.2017
Põhitekst
05.06.2012
Põhitekst
Põhitekst
EVS-EN ISO 9227:2006
This International Standard specifies the apparatus, the reagents and the procedure to be used in conducting the neutral salt spray (NSS), acetic acid salt spray (AASS) and copper‑accelerated acetic acid salt spray (CASS) tests for assessment of the corrosion resistance of metallic materials, with or without permanent or temporary corrosion protection. It also describes the method employed to evaluate the corrosivity of the test‑cabinet environment. It does not specify the dimensions of test specimens, the exposure period to be used for a particular product, or the interpretation of results. Such details are provided in the appropriate product specifications. The salt spray tests are particularly useful for detecting discontinuities, such as pores and other defects in certain metallic, organic, anodic oxide and conversion coatings. The neutral salt spray test is the test method in which a 5 % sodium chloride solution in the pH range from 6,5 to 7,2 is atomized under a controlled environment. It particularly applies to: - metals and their alloys, - metallic coatings (anodic and cathodic), - conversion coatings, - anodic oxide coatings, and - organic coatings on metallic materials. The acetic acid salt spray test is the test method in which a 5 % sodium chloride solution with the addition of glacial acetic acid in the pH range from 3,1 to 3,3 is atomized under a controlled environment. It is especially useful for testing decorative coatings of copper + nickel + chromium, or nickel + chromium. It has also been found suitable for testing anodic coatings on aluminum. The copper‑accelerated acetic acid salt spray test is the test method in which a 5 % sodium chloride solution with the addition of copper chloride and glacial acetic acid in the pH range from 3,1 to 3,3 is atomized under a controlled environment. It is useful for testing decorative coatings of copper + nickel + chromium, or nickel + chromium. It has also been found suitable for testing anodic coatings on aluminum. The salt spray methods are all suitable for checking that the comparative quality of a metallic material, with or without corrosion protection, is maintained. They are not intended to be used for comparative testing as a means of ranking different materials relative to each other with respect to corrosion resistance.
*
*
*
PDF
14,00 € koos KM-ga
Paber
14,00 € koos KM-ga
Hind: 2,40 € koos KM-ga
Standardi monitooring
Teised on ostnud veel
Põhitekst

EVS-EN ISO 1302:2002

Geometrical Product Specifications (GPS) - Indication of surface texture in technical product documentation
Uusim versioon Kehtiv alates 01.09.2002
Põhitekst

ISO 6362-1:2012

Wrought aluminium and aluminium alloys -- Extruded rods/bars, tubes and profiles -- Part 1: Technical conditions for inspection and delivery
Uusim versioon Kehtiv alates 22.06.2012
Põhitekst

ISO 6362-3:2012

Wrought aluminium and aluminium alloys -- Extruded rods/bars, tubes and profiles -- Part 3: Extruded rectangular bars -- Tolerances on shape and dimensions
Uusim versioon Kehtiv alates 22.06.2012
Põhitekst

ISO 6362-4:2012

Wrought aluminium and aluminium alloys -- Extruded rods/bars, tubes and profiles -- Part 4: Profiles -- Tolerances on shape and dimensions
Uusim versioon Kehtiv alates 22.06.2012